Super-SIX™  is EASY TO USE: 

The SIX in Super-SIX™

1) Polymer

• Improves flexural strength
• When dosed at 5% effective polymer load is 2.5% polymer solids.  High enough to act as curing admix eliminating the need of the 7-day wet cure allowing you to strip your forms much sooner
• Improved dispersion of color pigment and reduce color variation in panels

2) Plasticizer

• Greatly reduces water requirements resulting in stronger concrete
• Provides  very high spread rates, improved workability and greater fluidity

3) Shrinkage Reducer

• Greatly minimizes curling
• Reduction of shrinkage or map cracking

4) Defoamer

• Increases Density and virtually eliminates pin holes
• Improved density of mix (decreased permeability)

5) Wetting Agents

• Helps flow and dispersion of fibers
• Improves cement hydration
• Provides a homogeneous distribution and color strength of pigments

6) Water Proofer

• Increases water resistance and durability of cured concrete (hydrophobizing)

Super-SIX-Admix™  Recommendations: 

• https://concretecountertopsupply.com/supersixDose at 5-6% of cementitious weight (5-6 lbs. per hundred weight of cement)
• Recommend to start with a .28 -.30 Water:Cement ratio
• Can be used with just about any cementitious composition including CSA (Calcium Sulfa Alumina) and/or Pozzolans for increased performance.
• Super-SIX™  contains no Pozzolans or fibers and may be added as desired.  We recommend a minimum addition of .5% PVA fibers of cementitious for increased impact resistance & shrinkage crack control.  Additional Fishstone Plasticizer may be added for increased flow when using high fiber loading.

 A recommended sample recipe to create self-consolidating GFRC concrete is as follows:

• 100 lbs Federal White Cement
• 100 lbs silica sand (30 sieve or finer)  
• 28-30 lbs water
• 4 lbs ½ AR Glass Fibers(added last after other ingredients are thoroughly mixed)
• 5-6 lbs Super-SIX-Admix